Role of grain boundaries in hydrogen embrittlement of alloy 725: single and bi-crystal microcantilever bending study
<p>In situ electrochemical microcantilever bending tests were conducted in this study to investigate the role of grain boundaries (GBs) in hydrogen embrittlement (HE) of Alloy 725. Specimens were prepared under three different heat treatment conditions and denoted as solution-annealed (SA), ag...
محفوظ في:
| المؤلف الرئيسي: | |
|---|---|
| مؤلفون آخرون: | , , , , , |
| منشور في: |
2022
|
| الموضوعات: | |
| الوسوم: |
إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!
|
| الملخص: | <p>In situ electrochemical microcantilever bending tests were conducted in this study to investigate the role of grain boundaries (GBs) in hydrogen embrittlement (HE) of Alloy 725. Specimens were prepared under three different heat treatment conditions and denoted as solution-annealed (SA), aged (AG) and over-aged (OA) samples. For single-crystal beams in an H-containing environment, all three heat-treated samples exhibited crack formation and propagation; however, crack propagation was more severe in the OA sample. The anodic extraction of H presented similar results as those under the H-free condition, indicating the reversibility of the H effect under the tested conditions. Bi-crystal micro-cantilevers bent under H-free and H-charged conditions revealed the significant role of the GB in the HE of the beams. The results indicated that the GB in the SA sample facilitated dislocation dissipation, whereas for the OA sample, it caused the retardation of crack propagation. For the AG sample, testing in an H-containing environment led to the formation of a sharp, severe crack along the GB path.</p><h2>Other Information</h2> <p> Published in: International Journal of Hydrogen Energy<br> License: <a href="http://creativecommons.org/licenses/by/4.0/" target="_blank">http://creativecommons.org/licenses/by/4.0/</a><br>See article on publisher's website: <a href="https://dx.doi.org/10.1016/j.ijhydene.2022.01.251" target="_blank">https://dx.doi.org/10.1016/j.ijhydene.2022.01.251</a></p> |
|---|