Development of High-Flexural-Strength Titanium/Hydroxyapatite Biocomposites via Cold Spray Deposition with Titanium and Niobium Bond Coats

Achieving rapid, scalable fabrication of bone implants with a high flexural strength remains a major challenge. The persistent issues are mainly attributed to the incompatibility of the biomaterials (e.g., titanium (Ti) and niobium (Nb)) with the processing methods. The implants fabricated from solu...

Celý popis

Uloženo v:

Podrobná bibliografie
Hlavní autor:	Fatemeh Andami (22677082) (author)
Další autoři:	Prateek (7301339) (author), Eric Chia (22677085) (author), Stephen S. Nonnenmann (1701136) (author), Davoud M. Jafarlou (22677088) (author), James J. Watkins (1424419) (author)
Vydáno:	2025
Témata:	Biophysics Medicine Genetics Biotechnology Ecology Developmental Biology Hematology Computational Biology Space Science Biological Sciences not elsewhere classified Physical Sciences not elsewhere classified directly forms coatings approximately 310 mpa 9 ± 51 219 ± 25 0 ± 50 mechanical features similar primary ceramic particles including inferior adhesion higher young ’ 2 gpa ), utilizing intermediate ti ti substrate exhibits tunable mechanical properties promising fabrication method hap directly deposited g ., titanium pure ti coating surrounding bone damage lower flexural strength cold spray deposition mechanical properties ti coating cold spray scalable fabrication promising technique excellent adhesion biomaterial ’ 6 gpa thermal spray strength titanium natural bone flexural strength bone implants voids lead typically degrade significantly exceeds room temperature processing methods powder feedstocks persistent issues nb )) natural bones matrix composites major challenge mainly attributed induced defects implants fabricated implant loosening hap layer ceramic metal
Tagy:	Přidat tag Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!

Buďte první, kdo okomentuje tento záznam!

Development of High-Flexural-Strength Titanium/Hydroxyapatite Biocomposites via Cold Spray Deposition with Titanium and Niobium Bond Coats

Podobné jednotky