A Two-Step Femtosecond Laser-Based Deposition of Robust Corrosion-Resistant Molybdenum Oxide Coating
A two-step femtosecond-pulsed laser deposition (fs-PLD) process is reported for the rapid development of uniform, poreless, crack-free, and well-adhering amorphous coatings of source materials with a high melting point. The first step comprises a high-rate raw deposition of the source material via f...
محفوظ في:
| المؤلف الرئيسي: | |
|---|---|
| مؤلفون آخرون: | , , , , , |
| التنسيق: | article |
| منشور في: |
2023
|
| الموضوعات: | |
| الوصول للمادة أونلاين: | https://hdl.handle.net/11073/26313 |
| الوسوم: |
إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!
|
| الملخص: | A two-step femtosecond-pulsed laser deposition (fs-PLD) process is reported for the rapid development of uniform, poreless, crack-free, and well-adhering amorphous coatings of source materials with a high melting point. The first step comprises a high-rate raw deposition of the source material via fs-PLD, followed by a second step of scanning the raw sample with fs laser pulses of optimized fluence and scan parameters. The technique is applied to develop substoichiometric molybdenum oxide (MoOx, x < 3) coatings on mild steel. The thickness of the layer was ~4.25 μm with roughness around 0.27 μm. Comprehensive surface characterization reveals highly uniform and relatively moderate roughness coatings, implying the potential of these films as robust corrosion-resistant coats. Corrosion measurements in an aqueous NaCl environment revealed that the coated mild steel samples possess an average corrosion inhibition efficiency of around 95% relative to polished mild steel. |
|---|